Dual functional β-peptide polymer-modified resin beads for bacterial killing and endotoxin adsorption

BMC Materials volume 1, Article number: 5 (2019) Cite this article

Abstract

Background

Bacterial infections and endotoxin contaminations are serious problems in the production/manufacture of food, water, drinks, and injections. The development of effective materials to kill bacteria and adsorb endotoxins, particularly those caused by gram-negative bacteria, represents a major step toward improved safety. As synthetic mimic of host defense peptides, β-peptide polymers are not susceptible to bacterial resistance and exhibit potent bacteria-killing abilities upon antibiotic-resistant bacteria. This study investigated the potential of synthetic β-peptide polymer-modified polyacrylate (PA) beads to kill bacteria and remove endotoxin, i.e. lipopolysaccharide (LPS), produced by these bacteria.

Results

Synthetic β-peptide polymer-modified PA beads displayed strong antimicrobial activity against Escherichia coli and methicillin-resistant Staphylococcus aureus, as well as excellent biocompatibility. In addition, these β-peptide polymer-modified beads removed around 90% of the endotoxins, even at 200 EU/mL of LPS, a very high concentration of LPS.

Conclusions

β-peptide polymer-modified PA beads are efficient in bacterial killing and endotoxin adsorption. Hence, these modified beads demonstrate the potential application in the production/manufacture of food, water, drinks, and injections.

Background

Bacterial contamination of food packages, water treatment membranes, industrial pipes, and drug injection and medical devices is a serious problem globally and poses a threat to their biosafety and effectiveness [1,2,3,4,5]. To reduce or prevent bacterial contamination, antimicrobial drugs and antimicrobial coatings are widely used [6,7,8,9]. Unfortunately, indiscriminate use of antimicrobials has led to the emergence and spread of drug-resistant bacteria, which poses a challenge to human health [10,11,12,13]. In addition, biosafety-related factors such as immunomodulation are also very important.

Endotoxins, lipopolysaccharide (LPS) that function as major pathogenic immune factor, are released from the outer cell membrane of Gram-negative bacteria in response to an attack by antimicrobial agents. Endotoxins can activate complex immune effectors to generate a hyperinflammatory response and even provoke severe endotoxic shock and multiorgan dysfunction [14,15,16,17,18]. Therefore, multifunctional antibacterial materials are highly desirable for both efficient bacterial killing and biosafety considerations [19,20,21,22,23,24,25].

In contrast to conventional antibiotics, host-defense peptides (HDPs) have low susceptibility to antimicrobial resistance. Given this advantage, HDPs have received much research attention [26,27,28,29,30]. The versatile biological functions, such as antimicrobial activity combined with anti-inflammatory properties, of HDPs have made them promising candidates in relieving acute inflammation via inactivating or neutralizing endotoxins, in addition to killing bacteria [31,32,33,34]. The amphipathic structure of HDPs plays an important role in the process of endotoxin removal as well as in bacterial killing through hydrophobic and electrostatic interaction with toxic lipid A. This interaction occurs when the positively charged fragments within HDPs attract negatively charged phosphates of lipids A, and the hydrophobic fragments of HDPs bind with lipid A fatty acid moieties. However, HDPs derived from diverse sources have similar shortcomings: low stability upon proteolysis and a high cost. To address these problems, a series of synthetic mimics of HDPs have been developed. Several studies showed that these synthetic mimics of HDPs exhibited high endotoxin neutralization and killing efficacy against bacteria, thereby showing strong potential in antibacterial applications [35,36,37].

As synthetic mimics of HDPs, amphipathic β-peptide polymers display broad-spectrum and potent antimicrobial activities, in addition to favorable solution [38,39,40,41,42] and surface biocompatibility [43, 44]. In previous study, a thiol-terminated β-peptide polymer (50:50 DM-CH) was successfully modified to the flat surfaces of gold [43] and variable biomedical materials [44] and displayed excellent antimicrobial activity. In this study, we modified 50:50 DM-CH to the spherical surface of amino-functionalized polyacrylate (PA) resin beads and demonstrated their function in efficient bacterial killing and endotoxin adsorption.

Results and discussion

Preliminary work indicated that 50:50 DM-CH had potential antimicrobial activity. To test whether this β-peptide polymer could endow the surface of resin beads with antimicrobial activity and endotoxin adsorption, we prepared β-peptide polymer-immobilized PA resin beads (Fig. 1a) by shaking the beads at the presence of reacting agents in a tube for solid phase synthesis (Fig. 1c). The amine functionalized PA beads were first modified using a dual functional linker, 3-maleimidopropionic acid N-hydroxysuccinimide (MalOSu), to afford surface maleimide groups that reacted further with the thiol-terminated β-peptide polymer 50:50 DM-CH to produce antimicrobial polymer-modified beads. The presence of an S2p peak in the XPS spectra (Fig. 1b) of the β-peptide polymer modified beads confirmed successful antimicrobial polymer modification on the surface of the PA resin beads.

Fig. 1
figure 1

Synthesis of β-peptide polymer-modified PA beads. a The 20-mer 50:50 DM-CH was attached to the amino layer surface of the beads through the link with MalOSu. b XPS spectra of β-peptide polymer-modified PA beads. c Preparation process of β-peptide polymer-modified PA beads using the apparatus of solid-phase synthesis

Full size image

We examined the antimicrobial activity of the β-peptide polymer modified PA resin beads in phosphate buffered saline (PBS). The β-peptide polymer-modified beads killed MRSA completely within 2.5 h. When an aliquot of this suspension was added to fresh MH medium, no growth of MRSA was detected after 6 h, as indicated by the optical density (OD) that was identical to that of blank medium (Fig. 2a). The potent bacterial killing of the β-peptide polymer-modified PA resin beads was confirmed by zero colony forming unit (CFU) on the LB agar plate, which was incubated with an aliquot of suspension culture 24 h after OD reading (Fig. 2a). In sharp contrast, rapid growth of MRSA cells was observed on controls of PBS, after incubation with fresh MH medium for 6 h, as clearly indicated by both an increased OD value and a large number of bacterial colonies in the CFU counting test.

Fig. 2
figure 2

Antibacterial activity of β-peptide polymer-modified PA beads. a Illustration of antibacterial activity against MRSA at initial bacterial density of 1 × 105 CFU/mL with OD and CFU on a counting plate in PBS. b Antibacterial activity with different amounts of beads in 50% FBS at initial bacterial density of 1 × 104 CFU/mL. c SEM characterization of bacteria before and after 2.5 h of incubation

Full size image

Encouraged by these results, we investigated the antimicrobial ability of polymer-modified beads against E. coli and MRSA in the presence of serum, using 50% fetal bovine serum (FBS) in the assay medium. We observed 99.9% bacterial killing of both E. coli and MRSA by ≥ 50 mg beads per sample were used (Fig. 2b). We used scanning electron microscope (SEM) to assess morphological changes of E. coli and MRSA, incubated with the β-peptide polymer modified PA resin beads for 2.5 h. As compared to the intact membrane of bacteria incubated with bare beads, conspicuous shrinkage and damage of the bacterial membrane were observed among bacteria incubated with the β-peptide polymer-modified beads (Fig. 2c). This observation appointed to a membrane-active antimicrobial mechanism similar to that observed in our previous studies on the antimicrobial abilities of gold and polyurethane surfaces coated with β-peptide polymers [43, 44].

We then investigated endotoxins adsorption capacity of the modified beads using a FITC-LPS binding assay in PBS and a Tachypleus Amebocyte Lysate (TAL) kit assay in serum (Fig. 3a). The β-peptide polymer-modified beads adsorbed half of FITC-LPS at an initial LPS concentration of 1 μg/mL in PBS, whereas the bare beads and linker-modified beads showed almost no LPS adsorption (Fig. 3b). It is worth mentioning that the LPS concentration at 1 μg/mL in the above test was very high. We used this high LPS concentration on purpose to check the LPS adsorption upper limit of our peptide polymer-modified beads. The ability of LPS adsorption for β-peptide polymer-modified beads was evaluated in the presence of 50% FBS using a TAL assay at a reasonable LPS concentration, which was lower than that used in the FITC-LPS adsorption assay. Using 20 mg of beads per assay sample efficiently adsorbed around 90% of LPS at variable initial LPS concentration from 50 to 200 EU/mL.

Fig. 3
figure 3

Effects of β-peptide polymer modified PA beads on the binding of LPS. a Illustration of the interaction between LPS and beads. b Beads were incubated with FITC-LPS (1 μg/mL) in PBS. c Beads cultivated with different concentrations of LPS in serum using the TAL assay, no significant differences among tests using 50–200 EU/mL of LPS. **p < 0.01

Full size image

The results of the LPS adsorption assay in the presence of serum pointed to the potential application of these β-peptide polymer-modified beads in biomedical practice, where the biocompatibility of materials is a major concern. Therefore, we investigated the hemolysis and cytotoxicity of the polymer-modified beads using a static hemolysis assay and MTT assay. Beads with or without modification all showed less than 2% hemolysis (Fig. 4a). Interestingly, the cytotoxicity of bare beads against fibroblast cells was exhibited approximately 42%, whereas the cytotoxicity of the β-peptide polymer-modified beads was substantially lower and at a cell-compatible level (Fig. 4b).

Fig. 4
figure 4

Biocompatibility studies on PA resin beads. a Hemolysis rate of bare beads, linker-modified beads, and polymer-modified beads. TBS and TX-100 were used as negative and positive controls, respectively. b Cytotoxicity of NIH-3T3 fibroblast cells after incubation with the extracts of bare beads and polymer-modified beads using MTT assay. **p < 0.01

Full size image

Conclusion

We successfully modified PA beads with a synthetic β-peptide polymer, thiol-terminated 50:50 DM-CH. The resulting resin beads exhibited potent antibacterial activity against both Gram-negative E. coli and Gram-positive MRSA. Additionally, the modified beads demonstrated the ability for endotoxin adsorption. The biocompatibility and ease of synthesis of these polymer-modified beads point to their potential application as dual-functional materials for antibacterial and endotoxin adsorption.

Materials and methods

General

PA resin beads were purchased from Tianjin Nankai HECHENG S&T Co.,Ltd; bromoform, chlorosulfonyl isocyanate, trifluoroacetic anhydride, di-tert-butyl pyrocarbonate were purchased from Adamas-beta; Triphenylmethyl chloride and N-hydroxy succinimide (NHS) were obtained from Meryer Technologies in China; PBS was purchased from Thermo Fisher Scientific; LPS from Escherichia coli O111:B4, FITC-conjugates was purchased from Sigma-Aldrich; all others reagents and solvents were purchased from General-Reagent. In this study, two types of bacteria were used for in vitro antimicrobial test including Escherichia coli (E. coli ATCC 25922) and Staphylococcus aureus (S. aureus USA 300, methicillin-resistant strain, MRSA); NIH-3T3 fibroblast cells (3T3 ATCC CRL-1658) were obtained from the Cell Bank of Typical Culture Collection of Chinese Academy of Sciences (Shanghai, China) and were used for cytotoxicity study. Synthesized chemicals were purified using a SepaBean machine equipped with Sepaflash columns produced by Santai Technologies Inc. in China. CDCl3 or D2O were used as the solvent to collect the 1H NMR spectra on a Bruker spectrometer at 400 MHz. 1H NMR chemical shifts were referenced to the resonance for TMS internal standard for CDCl3 and residual protonated solvent for D2O; The mass spectrum data of compounds were collected using an Agilent HPLC 1100/MS G1956B mass spectrometer. Element analysis of the β-peptide polymer-modified PA resin beads was acquired using Thermo Fisher ESCALAB 250XI X-ray photoelectron spectroscopy (XPS). Morphology of bacteria on the modified resin beads was observed on a Hitachi S-4800 Field Emission Scanning Electron Microscope (FESEM). The TAL assay was provided by Xiamen Bioendo Technology. Co., Ltd. (Xiamen, China).

Synthesis of β-lactam monomers and poly-β-peptides

β-lactam monomers and poly-β-peptides were prepared by following the procedure in the literature [43, 45, 46]. The details are given in the Additional file 1, Synthesis S1. Synthesis of racemic β-lactam monomer (±) DMβ; Synthesis S2. Synthesis of β-Lactam monomers (±)-CHβ; Synthesis S3. Synthesis of polymerization co-Initiator; Synthesis S4. Synthesis of β-peptide polymers; Figure S1. 1H NMR spectrum of monomer (±) DMβ; Figure S2. 1H NMR spectrum of monomer (±) CHβ; Figure S3. 1H NMR spectrum of co-initiator; Figure S4. 1H NMR spectrum of β-peptide polymer 50:50 DM-CH.

Synthesis of the surface linker

3-Maleimidopropionic acid N-hydroxysuccinimide ester (MalOSu) was prepared according to the literature [47]. The details are given in the Additional file 1, Synthesis S4. Synthesis of the surface linker; Figure S5. 1H NMR spectrum of surface linker MalOSu.

Synthesis and characterization of poly-β-peptide immobilized on the surface of PA resin beads

Poly-β-peptide modified PA resin beads were synthesized from 400 to 600 μm diameter PA beads with an amino layer, of which the density was 0.8 mmol/g (Synthesis 1). Initially, 20 mg of beads were treated with MalOSu (26.5 mg, 0.1 mmol) in anhydrous CH2Cl2 overnight at rt, washed consecutively with CH2Cl2 and methanol, and dried. MalOSu-modified beads were reacted with a solution of Poly-β-peptide (SH-(DM0.5CH0.5)18) (30.8 mg, 0.008 mmol) in anhydrous DMF overnight at rt. After the synthesis, Poly-β-peptide modified PA resin beads were washed with DMF, CH2Cl2, and methanol, and dried in vacuo. The dried samples were then characterized by XPS analysis (the raw data of figures in Additional file 2).

Synthesis 1
figure 5

Synthesis of poly-β-peptide modified PA resin beads

Full size image

Examination on bactericidal efficacy of polymer modified surface in PBS and serum

Bacteria cells were inoculated in LB medium and cultured overnight at 37 °C with shaking at 150 rpm. An aliquot of 7.5 mL the bacterial suspension was centrifuged at 4000 rpm for 5 min to harvest bacteria cells as a pellet as the bottom of the tube and then the collected cells were suspended in PBS. After repeating above operation for 3 cycles, the bacteria cell suspension was adjusted to a cell density of 2 × 105 CFU/mL for antimicrobial assay. MRSA was used in the PBS system. The polymer modified PA beads (20 mg) were placed in each well containing 100 µL PBS to obtain the working suspension of 105 CFU/mL. After gently shaking at 37 °C for 2.5 h, an aliquot of 80 µL bacterial suspension after diluted 100 × from each well was added into the 96 well plate containing 100 µL LB medium, the plate was then incubated at 37 °C and observed OD value at 600 nm at regular intervals (the raw data of figures in Additional file 3). Above bacterial suspension finally extracted 10 µL after 24 h was spread onto agar plates and overnight cultured at 37 °C for colony counting to evaluate the viability of bacteria with the colony number. Additionally, MRSA and E. coli were used in the medium of 50% (FBS). Polymer-modified beads with different weight of 20 mg, 50 mg, 100 mg were added in the bacterial suspension at the final centration is 104 CFU/mL. An aliquot of 35 µL bacterial suspension with the dilution of 5X after incubating 2.5 h was enumerated on the LB agar plate to acquire the killing efficacy of the beads. Bacterial suspension without any beads was used as the negative control to give the colony number Ccontrol, and incubation with polymer-modified beads was marked as Csample. The killing efficacy of the polymer-tethered surface was calculated using the equation:

$${\text{Killing}}\;{\text{efficacy}}\,\left( \% \right) \, = \frac{{C_{\text{control}} - C_{\text{sample}} }}{{C_{\text{control}} }} \times 100.$$

SEM characterization of bacterial morphology

Bacterial cell suspension at the end of the above antimicrobial assay was collected and was fixed with 4% glutaraldehyde in phosphate buffer (PB) at 4 °C overnight. Then the fixed cells were rinsed with PBS three times and were dehydrated using a graded ethanol series of (30–100% ethanol). The sample was dried under N2 and was used directly for FESEM characterization.

FITC-LPS binding assay on polymer modified surface

200 µL of 1 μg/mL FITC-LPS in PBS was treated with 20 mg polymer-modified beads in each well of the 48-well plate [36]. After gently shaking away from the light, 100 µL solution was transferred from transparent 48-well plate to 96-well black plate. Adsorption of the FITC-conjugated LPS by modified beads was studied through exciting the FITC-LPS at 480 nm and monitoring the emission of FITC at 516 nm using a microplate reader (SpectraMax M2, USA) after 30 min. 200 μL of PBS without any beads and with modified beads was marked as \(F_{\text{control}}\) and \(F_{\text{sample}}\) respectively. The fluorescence intensity was calculated as follows:

$${\text{LPS}}\,{\text{adsorption}}\,\left( \% \right) = \frac{{F_{\text{control}} - F_{\text{sample}} }}{{F_{\text{control}} }} \times 100.$$

Adsorption of endotoxin (LPS) in serum

20 mg of polymer-modified beads were incubated in 50% FBS with 0–200 EU/mL endotoxin at 100 rpm for 3 h. The Chromogenic Tachypleus Amebocyte Lysate kit (Xiamen Bioendo Technology company, China) was used to measure endotoxin. Samples were heated at 70 °C to precipitate proteins followed by testing endotoxin concentration according to the manufacture’s introduction (the raw data of figures in Additional file 3).

Hemolysis assay on polymer modified surface

Fresh human blood was washed with Tris-buffered saline (TBS) for three times and the collected human red blood cell (hRBC) was diluted to 5% (v/v) with TBS. An aliquot of 100 µL HRBCs was added into the 48-well plate containing 20 mg of bead first immersed in the 100 µL TBS. Beads were incubated at 37 °C for 1 h with the gentle shake and then the collected cell suspension centrifuged at 3700 rpm for 5 min. An aliquot of 80 µL supernatant was transferred to each individual well of a 96-well plate to read the OD values at 405 nm (the raw data of figures in Additional file 3). The OD value for polymer modified surface, the OD value for negative control using TBS, and the OD value for positive control using TX-100 at 3.2 mg/mL were marked as \(A_{\text{test}}\), \(A_{\text{negative}}\) \(A_{\text{positive}}\), respectively. The percentage of hemolysis was calculated from the equation:

$${\text{Hemolysis}}\,\left( \% \right) = \frac{{A_{\text{sample}} - A_{\text{negative}} }}{{A_{\text{positive}} - A_{\text{negative}} }} \times 100.$$

Cytotoxicity evaluation

The cytotoxicity of beads was determined by the 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyl tetrazolium bromide (MTT) assay using NIH-3T3 cells [21]. Beads were first immersed in the DMEM culture medium at 37 °C for 24 h. extracts were then obtained and added into the wells of 96-well plate overnight containing the fibroblast solutions (~ 1×104 cell/well). After incubation, 100 μL of MTT (5 mg/mL, in PBS) was added into each well for another 4 h. Then 10 μL of MTT solution (5 mg/mL) was added to each well and the plate was incubated at 37 °C for 4 h. After removing the supernatant from each well, 150 μL/well of DMSO was added to dissolve the purple MTT-formazan crystals under shaking for 15 min. The absorbance of the solution in each well at 570 nm was measured using a microplate reader. The \(A_{\text{test}}\) represents the OD value corresponding to the β-peptide polymer modified beads and the bare beads, the \(A_{\text{control}}\) means the OD value corresponding to the control, the \(A_{\text{blank}}\) means the OD value corresponding to DMSO blank control. Cell viability was calculated from the equation:

$${\text{Cell}}\,{\text{viability}}\,\left( \% \right) = \frac{{A_{\text{test}} - A_{\text{blank}} }}{{A_{\text{control}} - A_{\text{blank}} }} \times 100.$$

Statistic analysis

Statistic analysis of the data was conducted using ANOVA and Tukey’s HSD posthoc test. A p value ≤ 0.05 is considered as statistically significant.

Abbreviations

PA:

polyacrylate

MRSA:

methicillin-resistant Staphylococcus aureus

LPS:

lipopolysaccharide

HDPs:

host defense peptides

MalOSu:

N-hydroxysuccinimide

OD:

optical density

CFU:

colony forming unit

SEM:

scanning electron microscope

References

  1. Guo LY, Yuan WY, Lu ZS, Li CM. Polymer/nanosilver composite coatings for antibacterial applications. Colloid Surf A. 2013;439:69–83.

    Article  CAS  Google Scholar 

  2. Coad BR, Kidd SE, Ellis DH, Griesser HJ. Biomaterials surfaces capable of resisting fungal attachment and biofilm formation. Biotechnol Adv. 2014;32(2):296–307.

    Article  CAS  Google Scholar 

  3. Valdes A, Ramos M, Beltran A, Jimenez A, Garrigos MC. State of the art of antimicrobial edible coatings for food packaging applications. Coatings. 2017;7(4):56/51–56/23.

    Article  CAS  Google Scholar 

  4. He C, Ji HF, Qian YF, Wang Q, Liu XL, Zhao WF, Zhao CS. Heparin-based and heparin-inspired hydrogels: size-effect, gelation and biomedical applications. J Mater Chem B. 2019;7(8):1186–208.

    Article  CAS  Google Scholar 

  5. Neoh KG, Li M, Kang ET, Chiong E, Tambyah PA. Surface modification strategies for combating catheter-related complications: recent advances and challenges. J Mater Chem B. 2017;5(11):2045–67.

    Article  CAS  Google Scholar 

  6. Wei T, Tang Z, Yu Q, Chen H. Smart antibacterial surfaces with switchable bacteria-killing and bacteria-releasing capabilities. ACS Appl Mater Interfaces. 2017;9(43):37511–23.

    Article  CAS  Google Scholar 

  7. Tu Q, Shen X, Liu Y, Zhang Q, Zhao X, Maitz MF, Liu T, Qiu H, Wang J, Huang N, et al. A facile metal–phenolic–amine strategy for dual-functionalization of blood-contacting devices with antibacterial and anticoagulant properties. Mater Chem Front. 2019;3(2):265–75.

    Article  CAS  Google Scholar 

  8. Qu Y, Wei T, Zhao J, Jiang S, Yang P, Yu Q, Chen H. Regenerable smart antibacterial surfaces: full removal of killed bacteria via a sequential degradable layer. J Mate Chem B. 2018;6(23):3946–55.

    Article  CAS  Google Scholar 

  9. Zhao X, Olsen I, Pratten J, Knowles JC, Young AM. Reactive calcium-phosphate-containing poly(ester-co-ether) methacrylate bone adhesives: setting, degradation and drug release considerations. J Mater Sci Mater Med. 2011;22(9):1993–2004.

    Article  CAS  Google Scholar 

  10. Stearns-Kurosawa DJ, Osuchowski MF, Valentine C, Kurosawa S, Remick DG. The pathogenesis of sepsis. In: Annu Rev Pathol. Edited by Abbas AK, Galli SJ, Howley PM, 6;2011:19–48.

    Article  CAS  Google Scholar 

  11. Martin GS. Sepsis, severe sepsis and septic shock: changes in incidence, pathogens and outcomes. Expert Rev Anti Infect Ther. 2012;10(6):701–6.

    Article  CAS  Google Scholar 

  12. Mayr FB, Yende S, Angus DC. Epidemiology of severe sepsis. Virulence. 2014;5(1):4–11.

    Article  Google Scholar 

  13. Ghosh C, Sarkar P, Issa R, Haldar J. Alternatives to conventional antibiotics in the era of antimicrobial resistance. Trends Microbiol. 2019;27(4):323–38.

    Article  CAS  Google Scholar 

  14. David SA. Towards a rational development of anti-endotoxin agents: novel approaches to sequestration of bacterial endotoxins with small molecules. J Mol Recognit. 2001;14(6):370–87.

    Article  CAS  Google Scholar 

  15. Shi JJ, Zhao Y, Wang YP, Gao WQ, Ding JJ, Li P, Hu LY, Shao F. Inflammatory caspases are innate immune receptors for intracellular LPS. Nature. 2014;514:187–92.

    Article  CAS  Google Scholar 

  16. Koziel J, Bryzek D, Sroka A, Maresz K, Glowczyk I, Bielecka E, Kantyka T, Pyrc K, Svoboda P, Pohl J, et al. Citrullination alters immunomodulatory function of LL-37 essential for prevention of endotoxin-induced sepsis. J Immunol. 2014;192(11):5363–72.

    Article  CAS  Google Scholar 

  17. Navas A, Ferrer R, Martinez ML, Goma G, Gili G, Masip J, Suarez D, Artigas A. Impact of hemoperfusion with polymyxin B added to hemofiltration in patients with endotoxic shock: a case-control study. Ann Intensive Care. 2018;8(1):1–9.

    Article  CAS  Google Scholar 

  18. Lelubre C, Vincent JL. Mechanisms and treatment of organ failure in sepsis. Nat Rev Nephrol. 2018;14(7):417–27.

    Article  Google Scholar 

  19. Zhao J, Song LJ, Shi Q, Luan SF, Yin JH. Antibacterial and hemocompatibility switchable polypropylene nonwoven fabric membrane surface. ACS Appl Mater Interfaces. 2013;5(11):5260–8.

    Article  CAS  Google Scholar 

  20. Ding XK, Duan S, Ding XJ, Liu RH, Xu FJ. Versatile antibacterial at materials: an emerging arsenal for combatting bacterial pathogens. Adv Funct Mater. 2018;28(40):1802140.

    Article  CAS  Google Scholar 

  21. Ding YY, Sun Z, Shi RW, Cui HQ, Liu YY, Mao HL, Wang B, Zhu DM, Yan F. Integrated endotoxin adsorption and antibacterial properties of cationic polyurethane foams for wound healing. ACS Appl Mater Interfaces. 2019;11(3):2860–9.

    Article  CAS  Google Scholar 

  22. Chen H, Cheng RY, Zhao X, Zhang YH, Tam A, Yan YF, Shen HK, Zhang YS, Qi J, Feng YH, et al. An injectable self-healing coordinative hydrogel with antibacterial and angiogenic properties for diabetic skin wound repair. NPG Asia Mater. 2019;11(1):1–12.

    Article  Google Scholar 

  23. Wu SM, Li AH, Zhao XY, Zhang CL, Yu BR, Zhao NN, Xu FJ. Silica-coated gold-silver nanocages as photothermal antibacterial agents for combined anti-infective therapy. ACS Appl Mater Interfaces. 2019;11(19):17177–83.

    Article  CAS  Google Scholar 

  24. Wei T, Yu Q, Chen H. Responsive and synergistic antibacterial coatings: fighting against bacteria in a smart and effective way. Adv Healthc Mater. 2019;8:e1801381.

    Article  CAS  Google Scholar 

  25. Wu J, Hu C, Tang Z, Yu Q, Liu X, Chen H. Tissue-engineered vascular grafts: balance of the four major requirements. Colloid Interface Sci Commun. 2018;23:34–44.

    Article  CAS  Google Scholar 

  26. Zasloff M. Antimicrobial peptides of multicellular organisms. Nature. 2002;415(6870):389–95.

    Article  CAS  Google Scholar 

  27. Boman HG. Antibacterial peptides: basic facts and emerging concepts. J Intern Med. 2003;254(3):197–215.

    Article  CAS  Google Scholar 

  28. Hancock RE, Sahl HG. Antimicrobial and host-defense peptides as new anti-infective therapeutic strategies. Nat Biotechnol. 2006;24(12):1551–7.

    Article  CAS  Google Scholar 

  29. Wiesner J, Vilcinskas A. Antimicrobial peptides: the ancient arm of the human immune system. Virulence. 2010;1(5):440–64.

    Article  Google Scholar 

  30. Chowdhury R, Ilyas H, Ghosh A, Ali H, Ghorai A, Midya A, Jana NR, Das S, Bhunia A. Multivalent gold nanoparticle-peptide conjugates for targeting intracellular bacterial infections. Nanoscale. 2017;9(37):14074–93.

    Article  CAS  Google Scholar 

  31. Hancock RE. Cationic peptides: effectors in innate immunity and novel antimicrobials. Lancet Infect Dis. 2001;1(3):156–64.

    Article  CAS  Google Scholar 

  32. Guani-Guerra E, Santos-Mendoza T, Lugo-Reyes SO, Teran LM. Antimicrobial peptides: general overview and clinical implications in human health and disease. Clin Immunol. 2010;135(1):1–11.

    Article  CAS  Google Scholar 

  33. Brandenburg K, Andra J, Garidel P, Gutsmann T. Peptide-based treatment of sepsis. Appl Microbiol Biotechnol. 2011;90(3):799–808.

    Article  CAS  Google Scholar 

  34. Martin L, van Meegern A, Doemming S, Schuerholz T. Antimicrobial peptides in human sepsis. Front Immunol. 2015;6:1–7.

    Google Scholar 

  35. De Bhattacharjya S. novo designed lipopolysaccharide binding peptides: structure based development of antiendotoxic and antimicrobial drugs. Curr Med Chem. 2010;17(27):3080–93.

    Article  Google Scholar 

  36. Ong ZY, Gao SJ, Yang YY. Short synthetic β-Sheet forming peptide amphiphiles as broad spectrum antimicrobials with antibiofilm and endotoxin neutralizing capabilities. Adv Funct Mater. 2013;23(29):3682–92.

    Article  CAS  Google Scholar 

  37. Lam SJ, O’Brien-Simpson NM, Pantarat N, Sulistio A, Wong EH, Chen YY, Lenzo JC, Holden JA, Blencowe A, Reynolds EC, et al. Combating multidrug-resistant gram-negative bacteria with structurally nanoengineered antimicrobial peptide polymers. Nat Microbiol. 2016;1(11):16162.

    Article  CAS  Google Scholar 

  38. Gelman MA, Weisblum B, Lynn DM, Gellman SH. Biocidal activity of polystyrenes that are cationic by virtue of protonation. Org Lett. 2004;6(4):557–60.

    Article  CAS  Google Scholar 

  39. Mowery BP, Lee SE, Kissounko DA, Epand RF, Epand RM, Weisblum B, Stahl SS, Gellman SH. Mimicry of antimicrobial host-defense peptides by random copolymers. J Am Chem Soc. 2007;129(50):15474–6.

    Article  CAS  Google Scholar 

  40. Liu RH, Chen XY, Hayouka Z, Chakraborty S, Falk SP, Weisblum B, Masters KS, Gellman SH. Nylon-3 polymers with selective antifungal activity. J Am Chem Soc. 2013;135(14):5270–3.

    Article  CAS  Google Scholar 

  41. Qian YX, Zhang DF, Wu YM, Chen Q, Liu RH. The design, synthesis and biological activity study of Nylon-3 polymers as mimics of host defense peptides. Acta Polym Sin. 2016;10:1300–11.

    Google Scholar 

  42. Zhang Q, Ma PC, Xie JY, Zhang S, Xiao XM, Qiao ZQ, Shao N, Zhou M, Zhang WJ, Dai CZ, et al. Host defense peptide mimicking poly-beta-peptides with fast, potent and broad spectrum antibacterial activities. Biomater Sci. 2019;7(5):2144–51.

    Article  CAS  Google Scholar 

  43. Qian YX, Qi F, Chen Q, Zhang Q, Qiao ZQ, Zhang S, Wei T, Yu Q, Yu S, Mao ZW, et al. Surface modified with a host defense peptide-mimicking β-peptide polymer kills bacteria on contact with high efficacy. ACS Appl Mater Interfaces. 2018;10(18):15395–400.

    Article  CAS  Google Scholar 

  44. Qi F, Qian YX, Shao N, Zhou RY, Zhang S, Lu ZY, Zhou M, Xie J, Wei T, Yu Q, et al. Practical preparation of infection-resistant biomedical surfaces from antimicrobial β-peptide polymers. ACS Appl Mater Interfaces. 2019;11(21):18907–13.

    Article  CAS  Google Scholar 

  45. Liu RH, Chen XY, Gellman SH, Masters KS. Nylon-3 polymers that enable selective culture of endothelial cells. J Am Chem Soc. 2013;135(44):16296–9.

    Article  CAS  Google Scholar 

  46. Zhang JH, Kissounko DA, Lee SE, Gellman SH, Stahl SS. Access to poly-beta-peptides with functionalized side chains and end groups via controlled ring-opening polymerization of beta-lactams. J Am Chem Soc. 2009;131(4):1589–97.

    Article  CAS  Google Scholar 

  47. Vigier-Carriere C, Garnier T, Wagner D, Lavalle P, Rabineau M, Hemmerle J, Senger B, Schaaf P, Boulmedais F, Jierry L. Bioactive seed layer for surface-confined self-assembly of peptides. Angew Chem Int Ed Engl. 2015;54(35):10198–201.

    Article  CAS  Google Scholar 

Download references

Acknowledgements

Not applicable.

Funding

This research was supported by the National Natural Science Foundation of China (No. 21574038, 21861162010), the National Key Research and Development Program of China (2016YFC1100401), the Natural Science Foundation of Shanghai (18ZR1410300), the “Eastern Scholar Professorship” from Shanghai local government (TP2014034), the national special fund for State Key Laboratory of Bioreactor Engineering, the Fundamental Research Funds for the Central Universities (22221818014). The funders had no role in study design, data collection and analysis, decision to publish, or preparation of the manuscript.

Author information

Author notes

  1. Yuxin Qian and Yue Shen have contributed equally

Authors and Affiliations

  1. State Key Laboratory of Bioreactor Engineering, Key Laboratory for Ultrafine Materials of Ministry of Education, Research Center for Biomedical Materials of Ministry of Education, School of Materials Science and Engineering, East China University of Science and Technology, Shanghai, 200237, China

    Yuxin Qian, Shuai Deng, Fan Qi, Ziyi Lu, Longqiang Liu, Ning Shao, Jiayang Xie & Runhui Liu

  2. Department of Nephrology, Shanghai Ninth People’s Hospital, School of Medicine, Shanghai Jiao Tong University, Shanghai, 200011, China

    Yue Shen, Tingyan Liu & Feng Ding

Authors
  1. Yuxin Qian
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Yue Shen
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Shuai Deng
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Tingyan Liu
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Fan Qi
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Ziyi Lu
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Longqiang Liu
    View author publications

    You can also search for this author in PubMed Google Scholar

  8. Ning Shao
    View author publications

    You can also search for this author in PubMed Google Scholar

  9. Jiayang Xie
    View author publications

    You can also search for this author in PubMed Google Scholar

  10. Feng Ding
    View author publications

    You can also search for this author in PubMed Google Scholar

  11. Runhui Liu
    View author publications

    You can also search for this author in PubMed Google Scholar

Contributions

RHL and FD proposed the research. YXQ, YS, RHL, and FD designed the experiments. YXQ, DS, QF, LZY carried out the preparation of monomer and polymer, synthesis of modified beads, XPS analysis, antimicrobial assay, hemolysis assay and then interpreted the data and drafted the manuscript. YS and TYL did antimicrobial assay in serum and TAL assay. LQL conducted the synthesis of the surface linker. NS performed cytotoxicity test, JYX made SEM characterization. All authors read and approved the final manuscript.

Corresponding authors

Correspondence to Feng Ding or Runhui Liu.

Ethics declarations

Availability of data and materials

All data generated or analysed during this study are included in this published article and its supplementary information files.

Competing interests

The authors declare that they have no competing interests.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Additional file 1.

Experimental data for the characterization of monomer, polymer and surface linker, including Synthesis S1. Synthesis of racemic β-lactam monomer (±) DMβ; Synthesis S2. Synthesis of β-Lactam monomers (±)-CHβ; Synthesis S3. Synthesis of polymerization co-Initiator; Synthesis S4. Synthesis of β-peptide polymers; Synthesis S4. Synthesis of the surface linker; Figure S1. 1H NMR spectrum of monomer (±) DMβ; Figure S2. 1H NMR spectrum of monomer (±) CHβ; Figure S3. 1H NMR spectrum of co-initiator; Figure S4. 1H NMR spectrum of β-peptide polymer 50:50 DM-CH; Figure S5. 1H NMR spectrum of surface linker MalOSu.

Additional file 2.

Raw data of Fig. 1. b XPS spectrum of polymer-modified beads displayed in the manuscript.

Additional file 3.

Raw data of other figures in the manuscript, including Fig. 2. a OD (optical density) of initial bacterial density of 1 × 105 CFU/mL MRSA; Fig. 2. b Antibacterial activity with different amounts of beads in 50% FBS at initial bacterial density of 1 × 104 CFU/mL; Fig. 3. b LPS adsorption of beads with FITC-LPS (1 μg/mL) in PBS; Fig. 3. c LPS adsorption of beads in different concentration of serum; Fig. 4. a Hemolysis rate of bare beads, linker-modified beads, and polymer-modified beads; Fig. 4. b Cytotoxicity of NIH-3T3 fibroblast cells after incubation with the extracts of bare beads and polymer-modified beads using MTT assay.

Rights and permissions

Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Qian, Y., Shen, Y., Deng, S. et al. Dual functional β-peptide polymer-modified resin beads for bacterial killing and endotoxin adsorption. BMC Mat 1, 5 (2019). https://0-doi-org.brum.beds.ac.uk/10.1186/s42833-019-0005-3

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://0-doi-org.brum.beds.ac.uk/10.1186/s42833-019-0005-3

BMC Materials

ISSN: 2524-8138

Contact us